Hana ʻia a me ka Hale Hana Hana Mea Hana Kiʻi Kiʻekiʻe ʻo Kina 0.5mm Invar 36

Uea ʻĀlohilohi 0.5mm Invar 36 no ka Sila ʻana i ka Mea Hana Kiʻi i Hōʻike ʻia

Uea ʻĀlohilohi 0.5mm Invar 36 no ka Sila ʻana i ka Mea Hana Pololei

Wehewehe Pōkole:

DIN 17745 4j36 Invar Alloy Wire Haʻahaʻa Hoʻonui Alloy Feni36 Wire

(Inoa Maʻamau: Invar, FeNi36, Invar Standard, Vacodil36)

ʻO 4J36 (Invar), i ʻike nui ʻia hoʻi ʻo FeNi36 (64FeNi ma ʻAmelika Hui Pū ʻIa), he hui hao nickel-hao i ʻike ʻia no kona coefficient haʻahaʻa kū hoʻokahi o ka hoʻonui wela (CTE a i ʻole α).

Kumu Hoʻohālike:ʻInvar

ʻOEM:ʻAe

Moku'āina:Palupalu 1/2 paʻakikī paʻakikī T-paʻakikī

Kōmike HS:74099000

Kumu:Kina

Ka nui o ka paʻa:8.1

E leka uila mai iā mākou

Nā kikoʻī huahana

Nā nīnau i nīnau pinepine ʻia

Nā Lepili Huahana

Hoʻohana ʻo 4J36 i ka hoʻoheheʻe ʻana oxyacetylene, ka hoʻoheheʻe ʻana o ke arc uila, ka hoʻoheheʻe ʻana a me nā ʻano hana hoʻoheheʻe ʻē aʻe. ʻOiai e pili ana ke koina o ka hoʻonui ʻana a me ka hoʻohuihui kemika o ka alloy e pono e pale ʻia ma muli o ka hoʻoheheʻe ʻana e hoʻololi i ka hoʻohuihui alloy, ʻoi aku ka maikaʻi o ka hoʻohana ʻana i ka hoʻoheheʻe ʻana o ke arc Argon. ʻOi aku ka maikaʻi o ka loaʻa ʻana o 0.5% a 1.5% titanium i loko, i mea e hōʻemi ai i ka porosity weld a me ka māwae.

ʻAno maʻamau%

Ni	35~37.0	Fe	Bal.	Co	-	Si	≤0.3
Mo	-	Cu	-	Cr	-	Mn	0.2~0.6
C	≤0.05	P	≤0.02	S	≤0.02

Ka helu hoʻonui

θ/ºC	α1/10-6ºC-1	θ/ºC	α1/10-6ºC-1
20~-60	1.8	20~250	3.6
20~-40	1.8	20~300	5.2
20~-20	1.6	20~350	6.5
20~-0	1.6	20~400	7.8
20~50	1.1	20~450	8.9
20~100	1.4	20~500	9.7
20~150	1.9	20~550	10.4
20~200	2.5	20~600	11.0

Nā waiwai kino maʻamau

Ka nui (g/cm3)	8.1
Ke kū'ē uila ma 20ºC (OMmm2/m)	0.78
Huna wela o ka resistivity(20ºC~200ºC)X10-6/ºC	3.7~3.9
*Ka hoʻokele wela, λ/ W/(mºC)**	11
Kiko Curie Tc/ ºC	230
Modulus Elastic, E/ Gpa	144

Ke kaʻina hana mālama wela
Hoʻoheheʻe ʻana no ka hoʻomaha ʻana i ke kaumaha	Hoʻomehana ʻia i 530 ~ 550ºC a paʻa no 1 ~ 2 h. Hoʻoanuanu
hoʻomehana ʻana	I mea e hoʻopau ai i ka paʻakikī, kahi e lawe ʻia ai i waho i ke kaʻina hana huki anu. Pono ka hoʻomehana ʻana i ka annealing i 830 ~ 880ºC i loko o ka vacuum, e paʻa i 30 min.
Ke kaʻina hana hoʻopaʻa	I loko o nā pāpaho pale a hoʻomehana ʻia i 830 ºC, e paʻa no 20min. ~ 1h, e kinai Ma muli o ke kaumaha i hana ʻia e ka hoʻopio ʻana, hoʻomehana ʻia i 315ºC, paʻa i 1 ~ 4h.
Nā Mālama	ʻAʻole hiki ke hoʻopaʻakikī ʻia e ka mālama wela Hiki i ka mālama ʻana i ka ʻili ke hana i ka oneblasting, polishing a pickling paha. Hiki ke hoʻohana ʻia ka Alloy 25% hydrochloric acid pickling solution ma 70 ºC e hoʻomaʻemaʻe i ka ʻili oxidized.