ferroalloys 0Cr21Al6Nb uwea pale pale fecral no ka umu uila
ferroalloys 0Cr21Al6Nb uwea pale pale fecral no ka umu uila
| Papa | 0Cr21Al6NbCo |
| Nui | 0.1-1.2mm |
| Ili | ʻālohilohi annealed |
| Kaumaha | 1-3kg/roll |
| Kū'ē | 1.45±0.07μΩ.m |
| ʻO ka wela kiʻekiʻe loa | 1350 ℃ |
| ʻO ka mānoanoa | 7.1g/cm³ |
| Ka ikaika tensile | 750N/mm² |
| ʻO ka elongation | ≥12% |
| Papa | ʻO ka wela kiʻekiʻe loa | Kū'ē | Lae hehee | Ka ikaika tensile | ʻO ka elongation |
| 0Cr21Al4 | 1100 ℃ | 1.23±0.06μΩ.m | 1500 ℃ | 750 | ≥12 |
| 0Cr25Al5 | 1250 ℃ | 1.42±0.07μΩ.m | 1500 ℃ | 750 | ≥12 |
| 0Cr23Al5 | 1300 ℃ | 1.35±0.06μΩ.m | 1500 ℃ | 750 | ≥12 |
| 0Cr21Al6NbCo | 1350 ℃ | 1.45±0.07μΩ.m | 1510 ℃ | 750 | ≥12 |
| 0Cr27Al7Mo2 | 1400 ℃ | 1.53±0.07μΩ.m | 1520 ℃ | 750 | ≥10 |
| KSC | 1350 ℃ | 1.44±0.05μΩ.m | 1510 ℃ | 750 | ≥16 |
| Cr20Ni80 | 1200 ℃ | 1.09±0.05μΩ.m | 1400 ℃ | 750 | ≥20 |
| Cr15Ni60 | 1150 ℃ | 1.12±0.05μΩ.m | 1390 ℃ | 750 | ≥20 |
| Cr20Ni35 | 1100 ℃ | 1.04±0.05μΩ.m | 1390 ℃ | 750 | ≥20 |
| Cr20Ni30 | 1100 ℃ | 1.04±0.05μΩ.m | 1390 ℃ | 750 | ≥20 |
| Papa | ʻO ka hui kemika% | ||||||||
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | |
| ≤ | |||||||||
| 0Cr21Al4 | 0.12 | 0.025 | 0.025 | 0.7 | ≤1.0 | 17-21 | ≤0.6 | 3-4 | kaulike |
| 0Cr25Al5 | 0.06 | 0.025 | 0.02 | 0.5 | ≤0.6 | 23-26 | ≤0.6 | 4.5-6.5 | kaulike |
| 0Cr23Al5 | 0.06 | 0.025 | 0.02 | 0.5 | ≤0.6 | 20.5-23.5 | ≤0.6 | 4.2-5.3 | kaulike |
| 0Cr21Al6Nb | 0.05 | 0.025 | 0.02 | 0.5 | ≤0.6 | 21-23 | ≤0.6 | 5-7 | kaulike |
| 0Cr27Al7Mo2 | 0.05 | 0.025 | 0.02 | 0.2 | ≤0.4 | 26.5-27.8 | ≤0.6 | 6-7 | kaulike |
| Cr20Ni80 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 20-23 | kaulike | ＜0.5 | ≤1.0 |
| Cr15Ni60 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 15-18 | 55-61 | ＜0.5 | kaulike |
| Cr20Ni35 | 0.08 | 0.02 | 0.015 | 1.0 | 1-3 | 18-21 | 34-37 | － | kaulike |
| Cr20Ni30 | 0.08 | 0.02 | 0.015 | 1.0 | 1-3 | 18-21 | 30-34 | － | kaulike |